Malleable iron

<h2 id="history">History</h2>
<p>Malleable iron was used as early as the 4th century <a href="/facts/Common_Era/e5DpqUoe">BCE</a>, and archaeologists have found malleable iron artifacts made in China between 4th century BCE and 9th century CE.<a class="footnote-ref" id="fnref:2" href="#fn:2"><sup>2</sup></a> By the <a href="/facts/Tang_dynasty/FFhmVfwM">Tang dynasty</a>, the use of malleable iron in China waned, although there are malleable iron artifacts dating to the 9th century.<a class="footnote-ref" id="fnref:3" href="#fn:3"><sup>3</sup></a> Malleable iron is mentioned in England in a patent dating to the 1670s.<a class="footnote-ref" id="fnref:4" href="#fn:4"><sup>4</sup></a> <a href="/facts/R%C3%A9aumur/JHbj9AzJ">Réaumur</a> conducted extensive research on malleable iron in 1720. He discovered that iron castings which were too hard to be worked could be softened by packing them into <a href="/facts/Iron_ore/rQMEvgMh">iron ore</a> or hammer slag and exposing them to high temperature for a number of days. Creating malleable iron began in the United States in 1826 when <a href="/facts/Seth_Boyden/BCmYQFY6">Seth Boyden</a> started a foundry for the production of harness hardware and other small castings.<a class="footnote-ref" id="fnref:5" href="#fn:5"><sup>5</sup></a>
</p>
<h2 id="castability-heat-treating-and-post-casting-operations">Castability, heat treating and post-casting operations</h2>
<p>Like similar irons with the carbon formed into spherical or nodular shapes, malleable iron exhibits good <a href="/facts/Ductility/SBJsahEk">ductility</a>. Incorrectly considered by some to be an "old" or "dead" material, malleable iron still has a legitimate place in the design engineer's toolbox. Malleable iron is a good choice for small castings or castings with thin cross sections (less than 0.25-inch, 6.35 mm). Other nodular irons produced with graphite in the spherical shape can be difficult to produce in these applications, due to the formation of carbides from the rapid cooling.
</p><p>Malleable iron also exhibits better fracture toughness properties in low temperature environments than other nodular irons, due to its lower silicon content. The ductile to brittle transition temperature is lower than many other ductile iron alloys.
</p><p>In order to properly form the spherical-shaped nodules of graphite (called temper graphite nodules or temper carbon nodules) in the annealing process, care must be taken to ensure that the iron casting will solidify with an entirely white iron cross section. Thicker sections of a <a href="/facts/Casting/cFJ0hPuU">casting</a> will cool slowly, allowing some primary graphite to form. This graphite forms random flake-like structures and will not transform to carbide during heat treatment. When stress is applied to such a casting in application, the fracture strength will be lower than expected for white iron. Such iron is said to have a 'mottled' appearance. Some countermeasures can be applied to enhance the formation of the all-white structure, but malleable iron foundries often avoid producing heavy sections.
</p><p>After the casting and heat treatment processes, malleable iron can be shaped through cold working, such as stamping for straightening, bending or <a href="/facts/Coining_(metalworking)/SX1jrDh3">coining</a> operations. This is possible due to malleable iron's desirable property of being less strain rate sensitive than other materials.
</p>
<h2 id="applications">Applications</h2>
<p>It is often used for small castings requiring good tensile strength and the ability to flex without breaking (ductility). Uses include electrical fittings, hand tools, pipe fittings, washers, brackets, fence fittings, power line hardware, farm equipment, mining hardware, and machine parts.<a class="footnote-ref" id="fnref:6" href="#fn:6"><sup>6</sup></a>
</p>
<h2 id="see-also">See also</h2>
<ul><li><a href="/facts/Ductile_iron/nLmcVYWP">Ductile iron</a></li>
<li><a href="/facts/Wrought_iron/zynpjrIv">Wrought iron</a></li></ul>

<h2 id="references">References</h2>

<ol>
<li id="fn:1"><p>Brown, Robert R. (1999). Foseco Ferrous Foundryman's Handbook. Butterworth-Heinemann. ISBN 0-7506-4284-X. <a href="0-7506-4284-X" target="_blank">0-7506-4284-X</a> <a href="#fnref:1" class="footnote-back-ref">↩</a></p></li>
<li id="fn:2"><p>Donald B. Wagner (1993). Iron and Steel in Ancient China. BRILL. p. 338. ISBN 978-90-04-09632-5. <a href="978-90-04-09632-5" target="_blank">978-90-04-09632-5</a> <a href="#fnref:2" class="footnote-back-ref">↩</a></p></li>
<li id="fn:3"><p>Donald B. Wagner (1993). Iron and Steel in Ancient China. BRILL. p. 338. ISBN 978-90-04-09632-5. <a href="978-90-04-09632-5" target="_blank">978-90-04-09632-5</a> <a href="#fnref:3" class="footnote-back-ref">↩</a></p></li>
<li id="fn:4"><p>Donald B. Wagner (1993). Iron and Steel in Ancient China. BRILL. p. 335. ISBN 978-90-04-09632-5. <a href="978-90-04-09632-5" target="_blank">978-90-04-09632-5</a> <a href="#fnref:4" class="footnote-back-ref">↩</a></p></li>
<li id="fn:5"><p>Journal and Proceedings of the Hamilton Scientific Association. 1927. {{cite journal}}: Missing or empty |title= (help) <a href="/wiki/Template:Cite_journal" target="_blank">/wiki/Template:Cite_journal</a> <a href="#fnref:5" class="footnote-back-ref">↩</a></p></li>
<li id="fn:6"><p>Harvey E Steinhoff; Gordon B Mannweiler (1960). Malleable Iron Castings. Malleable Founders Society. <a href="#fnref:6" class="footnote-back-ref">↩</a></p></li>
</ol>

Malleable iron open-in-new

Malleable iron