Stress corrosion cracking

<p>Stress corrosion cracking (SCC) is the growth of crack formation in a <a href="/facts/Corrosion/lIC7H4we">corrosive</a> environment. It can lead to unexpected and sudden failure of normally <a href="/facts/Ductile/SBJsahEk">ductile</a> metal <a href="/facts/Alloy/I7w7WQWR">alloys</a> subjected to a <a href="/facts/Tensile_stress/ErAXDbbd">tensile stress</a>, especially at elevated temperature. SCC is highly chemically specific in that certain alloys are likely to undergo SCC only when exposed to a small number of chemical environments. The chemical environment that causes SCC for a given alloy is often one which is only mildly <a href="/facts/Corrosion/lIC7H4we">corrosive</a> to the metal. Hence, metal parts with severe SCC can appear bright and shiny, while being filled with microscopic cracks. This factor makes it common for SCC to go undetected prior to failure. SCC often progresses rapidly, and is more common among alloys than pure metals. The specific environment is of crucial importance, and only very small concentrations of certain highly active chemicals are needed to produce catastrophic cracking, often leading to devastating and unexpected failure.
</p><p>The stresses can be the result of the crevice loads due to <a href="/facts/Stress_concentration/JUMQpYCP">stress concentration</a>, or can be caused by the type of assembly or <a href="/facts/Residual_stress/fNRwNanV">residual stresses</a> from fabrication (e.g. cold working); the residual stresses can be relieved by <a href="/facts/Annealing_(metallurgy)/2AfoCE4X">annealing</a> or other surface treatments. Unexpected and premature failure of chemical process equipment, for example, due to stress corrosion cracking constitutes a serious hazard in terms of safety of personnel, operating facilities and the environment. By weakening the reliability of these types of equipment, such failures also adversely affect productivity and profitability.
</p>

Stress corrosion cracking open-in-new

Stress corrosion cracking